26544-17-2 (壬二酸二异辛酯,Diisooctyl azelaate)

壬二酸二异辛酯;壬二酸二辛酯;壬二酸二异酸;壬二异辛,分子量：413;

Diisooctyl azelaate;Diisooctyl nonanedioate;Nonanedioic acid diisooctyl ester;DIISOOCTYL AZELATE;AZELAICACID,DIISOOCTYLESTER;Calciuma Formate;DIISOCTYL AZELATE;DIISOOCTYL AZELATE,TECH.;Diisooctylazelat;Einecs 247-774-8;(E)-2-(Buta-1,3-dienyl)cyclohexanol;Nonanedioic acid, 1,9-diisooctyl ester;26544-17-2;SCHEMBL50203;Nonanedioic acid, diisooctyl ester;NS00019796;106-03-6;bis(6-methylheptyl) nonanedioate;EINECS 203-355-1;DTXSID9067221;Bis-(6-methylheptyl)azelate;Bis(6-methylheptyl) azelate;AKOS015916163;DB-254026;G89988;CYNJQGPDCDNZBL-UHFFFAOYSA-N;1ST160454;1,9-BIS(6-METHYLHEPTYL) NONANEDIOATE;

CYNJQGPDCDNZBL-UHFFFAOYSA-N

1S/C25H48O4/c1-22(2)16-10-8-14-20-28-24(26)18-12-6-5-7-13-19-25(27)29-21-15-9-11-17-23(3)4/h22-23H,5-21H2,1-4H3

O(C(CCCCCCCC(=O)OCCCCCC(C)C)=O)CCCCCC(C)C

247-774-8

本品为优良的耐寒增塑剂。与聚氯乙烯、氯乙烯醋酸乙烯共聚物，聚苯乙烯、聚醋酸乙烯酯、醋酸丁酸纤维素、硝酸纤维素、乙基纤维素等有良好的相容性。其黏度低，沸点高，增塑效率高，水抽出性小，挥发性和迁移性小，而且具有优良的耐热性、耐光性、电绝缘性和对增塑糊的黏度稳定性，耐寒性比己二酸二辛酯（DOA）好。适用于人造革、薄膜、薄板、电线和电缆护套、增塑糊等，可赋予制品良好的低温性能。本品还可单独或与其他增塑剂配合用作丁腈橡胶、丁苯橡胶、氯丁橡胶等合成橡胶的增塑剂。

（1）壬二酸的制备0.6MPa的压缩空气经冷冻脱水后，再通过硅胶或分子筛干燥，然后进入臭氧发生器，在10000～12000V电压下，无声放电生成臭氧。臭氧经水洗后与油酸在溶剂中进行臭氧化，反应温度在10℃以下。臭氧化物于50～70℃下进行分解氧化，催化剂为醋酸锰，用量为臭氧化物的0.3%。用碱液从反应物中抽提出壬二酸，再经酸化、过滤、洗涤、烘干、即得壬二酸。（2）壬二酸二辛酯的制备将已制备的壬二酸投入反应釜，按摩尔比加入2.5倍的2-乙基己醇，再加入投料量0.3%的硫酸，于120～130℃、21.33kPa的压力下，反应4h。酯化至酸值小于2mgKOH/g时，即用碳酸钠中和至酸值小于0.15mgKOH/g。然后将所得的粗酯进行减压蒸馏，收集220～230℃（0.533kPa）馏分，再用活性炭在90～95℃进行脱色，过滤后，即得成品。