Development of highly gas-permeable polymers by metathesis copolymerization of 1-(p-trimethylsilyl)phenyl-1-propyne with tert-butyl and silyl group-containing diphenylacetylenes†,10.1039/D1RA06363D

热搜：

Lactoyl-CoA 全氟丁基戊烷白叶藤碱全氟己基辛烷新白叶藤碱壳寡糖特色专题-生物多肽

Development of highly gas-permeable polymers by metathesis copolymerization of 1-(p-trimethylsilyl)phenyl-1-propyne with tert-butyl and silyl group-containing diphenylacetylenes†

Yi Lin,Jianrong Dong,Toshikazu Sakaguchi,Tamotsu Hashimoto

RSC Advances Pub Date : 10/01/2021 00:00:00 , DOI:10.1039/D1RA06363D

Abstract

The development of highly gas-permeable membranes is required for gas separation applications. In this study, 1-(p-trimethylsilyl)phenyl-1-propyne (SPP) was copolymerized with diphenylacetylenes bearing tert-butyl (BDPA) and SiMe₃ (SDPA) groups at various feed ratios to obtain poly(SPP-co-BDPA) and poly(SPP-co-SDPA) copolymers, respectively. Free-standing membranes were fabricated from toluene solutions of the copolymers, the gas permeability of which increased as the SPP ratio decreased (P_O₂: 550–2100 barrers). Interestingly, poly(SPP-co-BDPA) and poly(SPP-co-SDPA) at a 1 : 4 ratio of SPP:BDPA and SPP:SDPA, respectively, showed higher permeabilities than the respective homopolymers. Desilylation of the poly(SPP-co-BDPA) membrane increased the gas permeability, whereas desilylation of the poly(SPP-co-SDPA) membrane had the opposite result.