We prepared a highly active molybdenum multisulfide (MoSx) hybrid material by an arc-melting method, which exhibits superior activity in acid media with a low overpotential of 156 mV at j = 10 mA cm−2, and a Tafel slope of 58 mV dec−1, surpassing most existing molybdenum-sulfide-based catalysts.