Zinc oxide nano-sheets (ZNS) loaded with Zeolitic Imidazole Framework 8 (ZIF8) nanocrystals, i.e. (ZNS@ZIF8) thin films, were successfully synthesized using electrodeposition and facile chemical bath deposition (CBD) for photoelectrochemical (PEC) splitting of water. The formation of ZNS nano-sheets and ZIF8 nano-crystals has been confirmed by field emission scanning electron microscopy (FE-SEM), low angle X-ray diffraction (XRD), micro-Raman spectroscopy, and Fourier transform infrared (FTIR) spectroscopy analysis. PEC activity of ZNS@ZIF8 photoanodes was evaluated using the linear sweep voltammetry (LSV) technique, and the photocurrent density is significantly enhanced when ZNS are decorated with ZIF8 nanocrystals. Electrochemical impedance spectroscopy (EIS) revealed that ZNS@ZIF8 had low charge transfer resistance compared to pristine ZNS counterparts. This led to considerably improved PEC performance of ZNS@ZIF8. Mott–Schottky (M–S) analysis of ZNS and ZNS@ZIF8 revealed a shift of flat band potential for the ZNS and ZNS@ZIF8 photoanodes, respectively. The shift of flat band potential indicates a clear shift in the Fermi level towards the conduction band, leading to an efficient charge transfer process across the electrolyte. The carrier density of ZNS and ZNS@ZIF8 photoanodes increases from 3.67 × 10¹⁹ cm⁻³ to 4.11 × 10²⁰ cm⁻³. The enhanced applied bias photon conversion efficiency (ABPE) of ZNS@ZIF8 photoanodes suggests that ZNS@ZIF8 can be a prospective candidate for PEC and optoelectronic applications.