In order to solve the problem of aseptic loosening of artificial joints resulting from the wear particles of artificial joint components in total joint replacement (TJR), we synthesized a new kind of metalo-organic particle (Sr/Zn-doped CPP/GNS) using spark plasma sintering (SPS) as a filler to enhance the comprehensive performance of UHMWPE. Sr/Zn-doped CPP/GNS was interfused evenly with UHMWPE particles and cured in a hot press instrument to prepare Sr/Zn-doped CPP/GNS/UHMWPE composites. FTIR and SEM were carried out to characterize Sr/Zn-doped CPP/GNS particles. EDS was carried out to characterize Sr/Zn-doped CPP/GNS/UHMWPE. The micro-structure, hardness, impact strength, tribology and bio-activities of Sr/Zn-doped CPP/GNS/UHMWPE composite materials were also investigated. The results confirmed the effectiveness of this method. The hardness, impact strength, and tribology of the composites were enhanced by adding homodispersed Sr/Zn-doped CPP/GNS particles into UHMWPE. In the meantime, Sr/Zn-doped CPP/GNS/UHMWPE composites could significantly promote the growth of osteoblasts due to the bio-activity of Sr/Zn-doped CPP/GNS. Furthermore, the addition of Sr/Zn-doped CPP/GNS particle-fillers into UHMWPE could promote the secretion of OPG from osteoblasts and inhibit the secretion of RANKL from osteoblasts, and thus increase the OPG/RANKL ratio. All the results above showed that Sr/Zn-doped CPP/GNS/UHMWPE composites with appropriate Sr/Zn-doped CPP/GNS content possessed superior physicochemical performances and bio-properties, and could be considered as promising materials to treat aseptic loosening in total joint replacement.