Exploiting high phosphorus content of phytic acid, it was grafted onto magnesium hydroxide (MH) by neutralization reaction to obtain MGPA, a flame retardant. A current study investigated the effect of MGPA on hydrophobicity, flame retardancy, and mechanical properties of MGPA-linear low-density polyethylene (LLDPE) composites. The LLDPE composite with 50 parts of MGPA has the better flame retardancy and thermal stability with a limiting oxygen index of 23.3%, which is higher than that of neat LLDPE (17%). In addition, MGPA could effectively promoted LLDPE to form a continuous and compact char residue during combustion, which reduce the peak of heat release rate and total smoke production value of LLDPE composite by 70% and 36%, respectively, and the char residue rate increase to 67.5%. Furthermore, the maximum of loss-rate showed by LLDPE composite with MGPA reduce to 1.25%/min while the value of LLDPE composite with MH is 1.8%/min. Meanwhile, the LLDPE composite with MGPA show remarkable elongation at break and hydrophobicity, which are 398% and 99°, respectively. In addition, this study presents a substantial flame retardancy and interfacial compatibility of MGPA for extending the applications of flame-retardant LLDPE composites.