10138-36-0 (4,5-环氧四氢邻苯二甲酸二辛酯,7-Oxabicyclo[4.1.0]heptane-3,4-dicarboxylicacid, 3,4-bis(2-ethylhexyl) ester)

2-溴-1-乙烯基-4-氟苯;4,5-环氧四氢邻苯二甲酸二(2-乙基己基)酯;4,5-环氧四氢邻苯二甲酸二辛（2-乙基已基）酯;4,5-环氧四氢邻苯二甲酸二辛酯;

7-Oxabicyclo[4.1.0]heptane-3,4-dicarboxylicacid, 3,4-bis(2-ethylhexyl) ester;bis(2-ethylhexyl) 7-oxabicyclo[4.1.0]heptane-3,4-dicarboxylate;di(2-Ethylhexyl)-4,5-epoxycyclohexane-1,2-dicarboxylate;4,5-Epoxycyclohexane-1,2-dicarboxylic acid, di-(2-ethylhexyl) ester;7-oxabicyclo(4.1.0)heptane-3,4-dicarboxylic acid, bis(2-ethylhexyl) ester;4,5-Epoxytetrahydrophthalate;7-Oxabicyclo[4.1.0]heptane-3,4-dicarboxylic acid bis(2-ethylhexyl) ester;E-PS;10138-36-0;NS00002993;4-18-00-04457 (Beilstein Handbook Reference);SCHEMBL2272253;EP 107;Di-(2-ethylhexyl)epoxyhexahydrophthalate;BRN 0332986;Sansocizer E-PS;EC 430-700-5;7-Oxabicyclo(4.1.0)heptane-3,4-dicarboxylic acid, di(2-ethylhexyl) ester;NIOSH/RN8221000;bis(2-ethylhexyl)-4,5-epoxycyclohexane-1,2-dicarboxylate;Di(2-ethylhexyl)4,5-epoxycyclohexane-1,2-dicarboxylate;RN82210000;EP-107;DTXSID60906099;

RRDGKBOYQLLJSW-UHFFFAOYSA-N

1S/C24H42O5/c1-5-9-11-17(7-3)15-27-23(25)19-13-21-22(29-21)14-20(19)24(26)28-16-18(8-4)12-10-6-2/h17-22H,5-16H2,1-4H3

O1C2CC(C(=O)OCC(CC)CCCC)C(C(=O)OCC(CC)CCCC)CC12

该品为聚氯乙烯的增塑剂兼稳定剂。增塑效率与DOP类似，混合性能优于DOP，可作主增塑剂。挥发性低，迁移性小，耐抽出性好。可赋予制品优良的光热稳定性、耐菌性和耐久性。特别适用于透明薄膜之类制品，也广泛用于人造革、板材、片材、电线和电缆料、涂料及各种成型品。加有本品的制品无油样解感或渗出现象。环氧四氢邻苯二甲酸酯是环氧增塑剂中最好的品种。环氧增塑剂分子中都含有环氧结构，主要包括环氧化油、环氧化脂肪酸单酯及环氧化四氢邻苯二甲酸酯，是一类发展的较快的增塑剂，其中较突出一个新品种是环氧化-1,2-聚丁二烯（C60H90O5）；将其作为聚氯乙烯的增塑剂，所得制品具有优良的耐水性和耐药品性。;

由顺丁烯二酸酐与丁二烯在100-110℃下进行双烯加成反应，制得四氢邻苯二甲酸酐。后者再与2-乙基己醇于减压（1.333-2.666kPa）和120-130℃下，由硫酸催化进行酯化反应。反应产物经水洗、蒸馏制得的四氢邻苯二甲酸二乙基己酯再在硫酸催化下与过氧化氢在甲酸，苯溶液中进行环氧化反应（55-60℃）而得粗品。粗品经分离、水洗、中和、脱苯、脱色、压滤，即为成品。原料消耗定额：顺丁烯二酸酐250kg/t、丁二烯116kg/t、2-乙基己醇654kg/t、30%双氧水570kg/t、甲酸100kg/t。