50813-16-6 (偏磷酸钠,Sodium polymetaphosphate)

六偏磷酸钠;多磷酸钠;偏磷酸钠;

Sodium polymetaphosphate;SODIUM POLYPHOSPHATE;Sodium polyphosphate, pure;liupianlinsuannna;polyphosphoricacidsodiumphotographicgrade;Sodium Kurrol's salt;Sodium metaphosphate, insoluble;50813-16-6;O0593;J139.264F;Metaphosphoric acid (HPO3), sodium salt (1:1);532IUT7IRV;Metaphosphoric acid,sodium salt;Sodium metaphosphate;Insoluble metaphosphate;Maddrell's salt;Metaphosphoric acid, sodium salt;Q4291659;Insoluble sodium metaphosphate;14550-21-1;HSDB 5055;EINECS 233-782-9;UNII-532IUT7IRV;SODIUM METAPHOSPHATE [WHO-DD];sodium phosphenate;Metaphosphoric acid (HPO3), sodium salt;SODIUM METAPHOSPHATE (NA(PO3));EINECS 238-595-6;10361-03-2;Sodium metaphosphate (NaPO3);Sodium phosphate (NaPO3);Kurrol's salt;DTXSID6040244;Sporix;SODIUM METAPHOSPHATE [VANDF];

AQMNWCRSESPIJM-UHFFFAOYSA-M

1S/Na.HO3P/c;1-4(2)3/h;(H,1,2,3)/q+1;/p-1

P(=O)(=O)[O-].[Na+]

2835391900

用作发电站，机车车辆，锅炉及化肥厂冷却水处理的高效软水剂。对Ca2+络合能力强，每100g能络合 5g钙，而且由于其螯合作用和吸附分散作用破坏了磷酸钙等晶体的正常生长过程，阻止磷酸钙垢的形成。用量 5mg/L，防止结垢率达95%～100%。

１．磷酸二氢钠法　将磷酸二氢钠加入聚合釜中，加热到700℃，脱水15-30min。然后用冷水骤冷，加工成型即得。２．磷酸酐法　黄磷经熔融槽加热融化后，流入燃烧炉，磷氧化后经沉淀、冷却，取出磷酐(P2O5)。将磷酐与纯碱按1∶0.8mol配比在搅拌器中混合后进入石墨坩埚。于750～800℃下间接加热，脱水聚合后，得六偏磷酸钠的熔融体。将其放入冷却盘中骤冷，即得透明玻璃状六偏磷酸钠。